We report the ferroelectric aging effect of dense BaTi0.995Mn0.005O3 ceramics with grain size varying from 2000 nm to 150 nm. Given the identical aging process, it is revealed that the significant aging effect with clear double-hysteresis loop, observed in coarse-grain sample, is substantially suppressed with decreasing grain size. This suppression can be attributed to the reduction of tetragonal distortion and the grain boundary barrier effect in fine-grain sample. Consequently, the weak thermodynamic driving force and the limited kinetic migration are unfavorable to a reversible domain switching, resulting in a normal hysteresis loop in small grained samples.